Correct-
There is structural wood, which isnt ideal, rotting stringers etc. Bad.
Then there is wood used as a fitting compression layer which is a good thing when used correctly as wood provides a good "crush" but stays structurally sound.
The there is core material- and in this particular category NOTHING man made has yet surpassed the properties of Balsa.
Sspecifically the areas of-
Tensil strength
Compression strength
Shearing strength
Shearing modulus
Density
The only area where man made materials can routinely compete is in density per square foot many are lighter.- butt most not by much.
Aside from that foam, and artificial core materials pale in comparison to balsas measurements. The occasional material comes close in an area or 2 (say oohhh a phenolic resin honeycomb- 200PSI shear- to Balsas 314 but overall when comparing everything but density per ft Balsa is the superior core material.
Problem with Balsa is that to lay it up properly and insure water integrity the lamination schedules MUST include vacuum bagging or resin infusion. There can be no guarantee of correct bonding in a hand laid hull with any core material without either of the two process mentioned above.
Balsa being wood-is more sensitive than foam to water incursion
BUT - if vac bagged has almost no chance of allowing any moisture to penetrate beyond what may be punctured as the individual end grains have the resin pulled completely through them they are in reality isolated individual pieces.